ASYRIL GFN 1 AE/V0 10% glass fibre flame retardant

PPO ASYRIL GFN 1 AE/V0 test method test condition unit values
ASTM ISO
PHYSICAL PROPERTIES          
specific gravity D792 1183 23° C gr/cm3 1,15
water absorption D570 62 24 h/23° C % 0,08
mold shrinkage D955 294-4   % 0,3÷0,5
melt flow index D1238 1133 220° C /10kg gr/10' -
melting point D3146 11357   °C -
MECHANICAL PROPERTIES          
tensile strength at yeld D638 527 23° C MPa 76
tensile strain at break D638 527 23° C % 2÷3
flexural modulus D790 178 23° C MPa 103
flexural strength D790 178 23° C MPa 4137
shear strength D732 - 23° C Mpa -
Rockwell hardness D785 2039/2 23° C R scale -
IZOD impact strength notched D256 180 3,2 mm +23°C J/m 107
THERMAL PROPERTIES          
Heat Deflection Temperature D648 75 1,8 MPa °C -
VICAT softening temperature D1525 306 10 N - 120°C/h °C 133
VICAT softening temperature D1525 306 50 N - 120°C/h °C 120
FLAMMABILITY          
flame resistance 1,6 mm UL94 -   class V0
flame resistance 3,2 mm UL94 -   class V0
glow wire test IEC 695-2-12 -   °C -
ELECTRICAL PROPERTIES          
dielectric strength D149 IEC 60243   KV/mm -
dielectric constant D150 IEC 60250 106 Hz   -
CTI Comparative Tracking Index   IEC 60112   V -
SUGGESTED PROCESSING CONDITIONS          
mold temperature       °C 60÷100
molding temperature       °C 260÷300
drying process temp/time       °C/h 2/90÷100

Specimens conditioning for >48 hours at 23° C / 50% R.H.

Data in this technical leaflet are coming from tests carried out in our internal lab on unpigmented and injected specimens, they show average values and they have to be considered as indicative only. Customers must ensure and satisfy themselves that the products to be purchased will fit for the particular purpose for which they intend to use them.
Altex s.r.l. accepts no liability for any of these values.